3003 3005 3105 Aluminum Coil
- Alloy Group: 3XXX
- Principal Alloying Element: Manganese
Description
Aluminum Alloy 3003 General Description:
What is Aluminum 3003?
Aluminum Alloy 3003 is a widely used medium strength aluminum alloy with manganese as its primary alloying element. It has good formability, and may be suitable for applications that require bending, spinning, drawing, stamping and roll forming.
Chemical Composition Limits:
Compositions are listed as weight percent. Limits are given as a maximum unless indicated as a range.
|
| Si | Fe | Cu | Mn | Mg | Cr | Zn | Ti | Others-Each | Others Total | Al Min |
| 3003 | 0.6 | 0.7 | 0.05-0.20 | 1.0-1.5 | – | – | 0.10 | – | 0.05 | 0.15 | Remain |
| 3005 | 0.6 | 0.7 | 0.3 | 1.0-1.5 | 0.2-0.6 | 0.10 | 0.25 | 0.10 | 0.05 | 0.15 | Remain |
| 3105 | 0.6 | 0.7 | 0.3 | 0.3-0.8 | 0.2-0.8 | 0.20 | 0.40 | 0.10 | 0.05 | 0.15 | Remain |
Composition according to Aluminum Association
Typical Mechanical Properties Data Of Aluminum 3003:
The following typical aluminum 3003 properties are not guaranteed since in most cases they are average for various sizes and methods of manufacture and may not be exactly representative of any particular product or size. The data is intended for comparing alloys and tempers and should not be used for design purposes.
Source: Aluminum Standards & Data and United Aluminum data base
| Alloy-Temper | Tensile Strength (ksi) | Yield Strength (ksi) | Elongation (%) Min |
| 3003-O | 14-19 | 5 Min | 30 |
| 3003-H14/H24 | 20-26 | 17 Min | 5 |
| 3003-H18/H28 | 27 Min | 24 Min | 5 |
| 3005-O | 17-24 | 6.5 Min | 14 |
| 3005-H14 | 24-31 | 21 Min | 5 |
| 3105-O | 14-21 | 5 Min | 20 |
| 3105-H14 | 22-29 | 18 Min | 5 |
| 3105-H24 | 22 Min | 18 Min | 8 |